Core-shell nanoparticles with multiple cores and a method for fabricating them

ABSTRACT

The present invention is directed toward core-shell nanoparticles, each comprising a ligand-capped metal shell surrounding a plurality of discrete, nonconcentric, metal-containing cores. Methods of making and using these nanoparticles are also disclosed.

This application claims the benefit of U.S. Provisional Patent Application Ser. No. 60/890,699, filed Feb. 20, 2007, which is hereby incorporated by reference in its entirety.

This invention was made with government support under award CHE0349040 awarded by the National Science Foundation. The government has certain rights in this invention.

FIELD OF THE INVENTION

The present invention relates to core-shell nanoparticles with multiple cores and a method for fabricating them.

BACKGROUND OF THE INVENTION

Nanoparticles exhibit intriguing changes in electronic, optical, and magnetic properties as a result of the nanoscale dimensionality (Daniel et al., Chem. Rev. 104:293 (2004); Xia et al., Adv. Mater. 12:693 (2000)). The ability to engineer size and monodispersity is essential for the exploration of these properties. The preparation of magnetic nanoparticles and nanocomposites has attracted both fundamental and practical interest because of potential applications in areas such as ferrofluids, medical imaging, drug targeting and delivery, cancer therapy, separations, and catalysis (Kim et al., J. Magn. Magn. Mater. 225:256 (2001); Niemeyer, Angew. Chem. Int. Ed. 40:4128 (2001); Neuberger et al., J. Magn. Magn. Mater. 293:483 (2005); Tartaj et al., J. Magn. Magn. Mater. 290:28 (2005); Dobson, Drug Dev. Res. 67:55 (2006)). However, one of the major obstacles is the lack of flexibility in surface modification and biocompatibility. Gold coating on magnetic particles provides an effective way to overcome such an obstacle via well-established surface chemistry to impart magnetic particles with the desired chemical or bio-medical properties (Daniel et al., Chem. Rev. 104:293 (2004); Xia et al., Adv. Mater. 12:693 (2000)). There have been reports on the synthesis of gold-coated magnetic core-shell particles by various methods, e.g. gamma ray, laser ablation, sonochemical method, layer-by-layer electrostatic deposition, chemical reduction, and micelle methods (Kinoshita et al., J. Magn. Magn. Mater. 293:106 (2005); Zhang et al., J. Phys. Chem. B 110:7122 (2006); Caruntu et al., Chem. Mater. 17:3398 (2005); Spasova et al., J. Mater. Chem. 15:2095 (2005); Stoeva et al., J. Am. Chem. Soc 127:15362 (2005); Lyon et al., Nano Letters 4:719 (2004); Mandal et al., J. Colloid Interface Sci. 286:187 (2005)). Recently reported was the synthesis of monodispersed core-shell Fe oxide-Au nanoparticles via coating pre-synthesized iron oxide nanoparticles (5-7 nm sizes) with gold shells (1-2 nm) (Wang et al., J. Phys. Chem. B 109:21593 (2005)). However, many of the magnetic core or shell dimensions have been limited to <15 nm. This limitation poses a serious barrier to magnetic applications where the size tunability, especially in larger sizes (up to ˜100 nm) with sufficient magnetization, is required.

The present invention is directed to overcoming these deficiencies in the art.

SUMMARY OF THE INVENTION

One aspect of the present invention is directed toward core-shell nanoparticles, each comprising a ligand-capped metal shell surrounding a plurality of discrete, nonconcentric, metal-containing cores.

Another aspect is directed to a method of producing core-shell nanoparticles, each comprising a ligand-capped metal shell surrounding one or more metal-containing cores. This method includes providing ligand-capped metal-containing core material nanoparticles and ligand-capped metal shell material nanoparticles. These nanoparticles are reacted under conditions effective to produce the core-shell nanoparticles comprising a ligand-capped metal shell surrounding one or more metal-containing cores.

A further aspect of the present invention is directed to a method of separating a target molecule from a sample. In accordance with this method, core-shell nanoparticles, each comprising a ligand-capped metal shell surrounding a plurality of discrete, nonconcentric, metal-containing cores are provided, with a first binding material bound to the ligand-capped shell. The binding material that specifically binds to the target molecule is incubated with the sample in a reaction vessel under conditions effective for the first binding material to bind to the target molecule. The reaction vessel is contacted with a magnet under conditions effective to immobilize the nanoparticles in the reaction vessel. The immobilized nanoparticles may be recovered.

Disclosed herein is a novel thermal approach to the fabrication of core-shell magnetic nanoparticles with not only high monodispersity but also size tunability in the 5-100 nm range. The basic idea explores the viability of hetero-interparticle coalescence between gold and magnetic nanoparticles under encapsulating environment for creating core-shell type nanoparticles in which the magnetic core consists of single or multiple metal cores with a pomegranate-like interior structure depending on the degree of coalescence (see FIG. 1).

This approach is new and differs from previous methods for synthesizing gold-coated Fe-Oxide particles in two significant ways: First, the present method uses a thermal evolution method starting from Fe-Oxide nanoparticles and Au nanoparticles as precursors, whereas the previous synthesis method uses Fe-Oxide nanoparticles and Au(Ac)₃ molecules as precursors. Second, the present method produces golden magnetic particles with either single core or multiple cores, whereas the previous method produces golden magnetic particles with only a single core.

This approach is also new in comparison with the homo-interparticle coalescence demonstrated for evolving the sizes of gold nanoparticles by a thermally-activated evolution (Zhong et al, Chem. Comm. 13:1211 (1999); Maye et al., Langmuir 16:490 (2000), which are hereby incorporated by reference in their entirety). In the previous method interparticle coalescence of metals or alloys is utilized for evolving the sizes of gold or alloy nanoparticles. In the present method, it is hetero-coalescence between Fe-oxide nanoparticles and gold nanoparticles for evolving single core Fe-Oxide-Au nanoparticles and multiple-core (Fe-Oxide)_(n)-Au nanoparticles. The competition between growing Au, Fe-oxide-Au, and the pomegranate-like core-shell nanoparticles is determined by solution temperature, composition and capping structures. This approach could serve as a simple and effective strategy for monodispersed Fe-oxide-Au nanoparticles of controlled sizes.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic drawing illustrating the hetero-interparticle coalescence of nanoparticles. Component 1A represents ligand-capped metal shell material nanoparticles. Component 1B represents ligand-capped metal-containing core material nanoparticles. Component A and B combine to form nanoparticles (i.e. Component C) comprising a ligand-capped metal shell surrounding a single metal-containing core. Component C coalesces to form component D which is a nanoparticle comprising a ligand-capped metal shell surrounding a plurality of discrete, nonconcentric, metal-containing cores.

FIG. 2A shows a schematic drawing of a core-shell nanoparticle with binding material and antibodies bound to the core-shell nanoparticle. FIG. 2B-C are schematic drawings of methods of concentrating target analytes using magnetic nanoparticles.

FIGS. 3A-B are TEM micrographs of gold nanoparticles produced by thermal processing (149° C.) of Au_(2nm)-DT nanoparticles. FIG. 3A shows the precursor nanoparticles 2.0±0.4 nm and FIG. 3B shows the product nanoparticles (6.4±0.4 nm).

FIGS. 4A-B are TEM images of OA/OAM-capped Fe₂O₃ nanoparticles produced by thermal processing (149° C.): before (FIG. 4A, 4.4±0.3 nm) and after (FIG. 4B, 4.5±0.5 nm) thermal processing.

FIGS. 5A-C are TEM images for precursor Fe₂O₃ (FIG. 5A), Au (FIG. 5B), and thermally-evolved Au-coated Fe₂O₃ nanoparticles using 25:1 ratio of Au to Fe₂O₃ nanoparticles (FIG. 5C).

FIGS. 6A-B are TEM images of the nanoparticles thermally evolved from the same nanoparticles precursors but with two different molar ratios of Au nanoparticles to Fe₂O₃ nanoparticles, (FIG. 6A) Au:Fe₂O₃=25:1, and (FIG. 6B) Au:Fe₂O₃=132:1.

FIGS. 7A-D are TEM images of nanoparticles obtained from the same precursor molar ratios (Au:Fe₂O₃=5:1) but using different capping agents on Fe₂O₃: OA-capped Fe₂O₃ (FIG. 7A), OA-capped Fe₂O₃ (FIG. 7B), OAM-capped Fe₂O₃ (FIG. 7C), and OA/OAM-capped Fe₂O₃ in a ˜2× reaction volume (FIG. 7D).

FIG. 8 is a schematic illustration of the dithiolate-gold based binding chemistry for the thin film assembly of Fe₂O₃@Au (A), Au (B) and Fe₂O₃ (C) nanoparticles on a substrate.

FIGS. 9A-B are SERS spectra for MBA label which are incorporated onto OA-OAM capped Fe₂O₃@Au nanoparticles (FIG. 9A) and protein-A capped Au nanoparticles (FIG. 9B).

FIGS. 10A-C is a photograph showing magnetic properties of Fe₂O₃@Au nanoparticles dissolved in toluene (FIG. 1A), suspended in ethanol-toluene (FIG. 10B), and after applying a magnet to the suspension of FIG. 10B (FIG. 10C).

FIGS. 11A-B are FTIR spectra of OA/OM-capped core@shell Fe₂O₃@Au particles before (FIG. 11A) and after (FIG. 11B) ligand exchange reaction with MUA.

FIG. 12 is an illustration of the reactions and product separation of antibody-labeled Fe₂O₃@Au nanoparticles in two different reaction systems: (A1-B1): reaction with protein A capped gold nanoparticles, and (A2-B2): reaction with BSA capped gold nanoparticles. In both cases, the SERS Label (L) mercaptobenzoic acid (MBA); Antibody (Ab): anti-rabbit IgG.

FIG. 13 is a UV-Vis spectra monitoring the reaction between Au/Protein-A/L and Fe₂O₃@Au/Ab (A1). Inset: the spectra monitoring the reaction between Au/BSA/L and Fe₂O₃@Au/Ab (A2). The spectra were recorded as a function of time (within 1 hr). The arrows indicate the direction of the spectral evolution as a function of time.

FIG. 14 is a SERS spectra of the products from the reactions between Au/Protein-A/L and Fe₂O₃@Au/Ab and between Au/BSA/L and Fe₂O₃@Au/Ab (A2). A magnet was used to collect the particles, which were then deposited on a Au substrate. SERS Label (L): MBA. Antibody (Ab): anti-rabbit-IgG.

DETAILED DESCRIPTION OF THE INVENTION

One aspect of the present invention is directed toward core-shell nanoparticles, each comprising a ligand-capped metal shell surrounding a plurality of discrete, nonconcentric, metal-containing cores. The core-shell nanoparticles may be present in a monodispersion with controlled diameters ranging from 5 nm to 100 nm.

The metal-containing cores may be magnetic, paramagnetic or superparamagnetic. The metal of the metal-containing cores may be iron (e.g., Fe₃O₄ or Fe₂O₃), magnesium, cobalt, or mixtures thereof.

The metal of the metal shell may be gold, silver, platinum, rhodium, palladium, vanadium, titanium, iron, cobalt, magnesium, ruthenium, chromium, molybdenum, tantalum, zirconium, manganese, tin, or mixtures thereof.

The capping ligand may be decanethiolate, oleylamine, oleic acid, acrylates, N,N-trimethyl(undecylmercapto)ammonium (TUA), tetrabutylammonium tetrafluoroborate (TBA), tetramethylammonium bromide (TMA), cetyltrimethylammonium bromide (CTAB), citrates, poly methacrylate, ascorbic acid, DNA, 2-mercaptopropionic acid (MPA), 3-mercaptopropionic acid (MPA), 11-mercaptoundecanoic acid (MUA), 10-mercaptodecane-1-sulfonic acid, 16-mercaptohexadecanoic acid, diimide, N-(2-mercaptopropionyl)glycine(tiopronin), 2-mercaptoethanol, 4-mercapto-1-butanol, dodecyl sulfate, amino acids, homocysteine, homocystine, cysteine, cystine, glutathione, mercaptobenzoic acid (MBA), Protein A, bovine serum albumin (BSA), or anti-rabbit-IgG (Ab).

The core-shell nanoparticles may further comprise a binding material bound to the ligand-capped shell. The binding material may be proteins, peptides, antibodies, or antigens.

Another aspect is directed to a method of producing core-shell nanoparticles, each comprising a ligand-capped metal shell surrounding one or more metal-containing cores. This method includes providing ligand-capped metal-containing core material nanoparticles and ligand-capped metal shell material nanoparticles. These nanoparticles are reacted under conditions effective to produce the core-shell nanoparticles comprising a ligand-capped metal shell surrounding one or more metal-containing cores.

As shown in FIG. 1, the method of the present invention provides for hetero-interparticle coalescence of ligand-capped metal shell material nanoparticles, e.g., decanethiolate (DT)-capped Au (Component A) and ligand-capped metal-containing core material nanoparticles, e.g., oleic acid or oleylamine (OA/OM)-capped Fe₂O₃ (Component B). Thermal evolution results in the formation of nanoparticles comprising a ligand-capped metal shell surrounding a single metal-containing core (Component C). These single-core nanoparticles can undergo further thermal evolution to form nanoparticles comprising a ligand-capped metal shell surrounding a plurality of discrete, nonconcentric, metal-containing cores (Component D).

The specific materials used to form these ligand-capped metal shell surrounding one or more metal containing cores and the structure of the nanoparticles themselves are substantially the same as those described above.

The reaction conditions may include combining the ligand-capped metal-containing core material nanoparticles and the ligand-capped metal shell material nanoparticles in a solvent to form a reaction mixture. The reaction mixture is heated under conditions effective to form the core-shell nanoparticles comprising a ligand-capped metal shell surrounding one or more metal-containing cores.

The solvent may include toluene, tetraoctylammonium bromide, and/or decanethiols and may be heated to a temperature of 140-160° C.

The core-shell nanoparticles may be subjected to one or more sizing operations, such as centrifugation.

A further aspect of the present invention is directed to a method of separating a target molecule from a sample. In accordance with this method, core-shell nanoparticles, each comprising a ligand-capped metal shell surrounding a plurality of discrete, nonconcentric, metal-containing cores are provided, with a first binding material bound to the ligand-capped shell. The binding material that specifically binds to the target molecule is incubated with the sample in a reaction vessel under conditions effective for the first binding material to bind to the target molecule. The reaction vessel is contacted with a magnet under conditions effective to immobilize the nanoparticles in the reaction vessel. The immobilized nanoparticles may be recovered.

The method may include removing liquids from the reaction vessel. Once the nanoparticles with binding materials are bound to the target in a sample solution and the vessel is contacted with a magnet thereby immobilizing the nanoparticles-target complex, all or some of the sample solution can be removed for further purification, analysis, or other use. The liquids can be removed by various means well known in the art including pumping, pouring, pipetting, or evaporation.

Furthermore, the target molecules may be separated from the nanoparticles. Target molecules may be reversibly bound to the binding material or the binding material may be reversibly bound to the nanoparticles, allowing separation of the target molecules from the nanoparticles by various methods known in the art such as salvation, exchange, heating, or digestion.

The binding material may be proteins, peptides, antibodies, antigens or other suitable material known in the art.

Magnetic separation techniques are commonly used for the purification, quantification, or identification of various substances (see Ito et al., J. Biosci. Bioeng. 100(1): 1-11 (2005); Alexiou et al., J. Nanosci. Nanotechnol., 6:2762 (2006); and Risoen et al., Protein Expr. Purif. 6(3):272-7 (1995), which are hereby incorporated by reference in their entirety). The term “magnetic particles” is meant to include particles that are magnetic, paramagnetic, or superparamagnetic properties. Thus, the magnetic particles are magnetically displaceable but are not necessarily permanently magnetizable. Methods for the determination of analytes using magnetic particles are described, for example, in U.S. Pat. No. 4,554,088, which is hereby incorporated by reference in its entirety.

The magnetic particle may be bound to an affinity ligand, the nature of which will be selected based on its affinity for a particular analyte whose presence or absence in a sample is to be ascertained. The affinity molecule may, therefore, comprise any molecule capable of being linked to a magnetic particle which is also capable of specific recognition of a particular analyte. Affinity ligands, therefore, include monoclonal antibodies, polyclonal antibodies, antibody fragments, nucleic acids, oligonucleotides, proteins, oligopeptides, polysaccharides, sugars, peptides, peptide encoding nucleic acid molecules, antigens, drugs, and other ligands.

The target material may optionally be a material of biological or synthetic origin. For examples, such target materials may be antibodies, amino acids, proteins, peptides, polypeptides, enzymes, enzyme substrates, hormones, lymphokines, metabolites, antigens, haptens, lectins, avidin, streptavidin, toxins, poisons, environmental pollutants, carbohydrates, oligosaccharides, polysaccharides, glycoproteins, glycolipids, nucleotides, oligonucleotides, nucleic acids and derivatised nucleic acids, DNA, RNA, natural or synthetic drugs, receptors, virus particles, bacterial particles, virus components, cells, cellular components, and natural or synthetic lipid vesicles.

Magnetic particles have potential to be used in imaging and analytical detection assays as well. For example, in a Surfaced Enhanced Raman Spectroscopy (SERS)-based assay, increasing analyte concentration in solution or local analyte concentration at an assay surface can significantly improve the limits of detection of different analytes, especially of large biomolecules such as bacteria and viruses. FIG. 2A shows a representation of antibodies, for example, bound to a magnetic core-shell nanoparticle. Such a system could be used to bind a target forming a nanoparticle-target complex. Application of a magnetic field will allow immobilization of the nanoparticle-target complex (FIG. 2B). Alternatively, through the application of a magnetic field, the nanoparticle-target complex can be concentrated at the site of an assay surface (FIG. 2C) allowing for detection or improvement of the limits of detection.

During recent years, there has been in increase in interest regarding the use of magnetic nanoparticles as contrast agents for use in conjunction with magnetic resonance imaging (MRI) techniques (Ito et al., J. Biosci. Bioeng. 100:1-11 (2005), which is hereby incorporated by reference in its entirety). Magnetic nanoparticles have also been proposed for use in direct sensing methods for diagnosis of cancer (Suzuki et al., Brain Tumor Pathol. 13:127 (1996), which is hereby incorporated by reference in its entirety) and for novel tissue engineering methodologies utilizing magnetic force and functionalized magnetic nanoparticles to manipulate cells (Ito et al., J. Biosci. Bioeng. 100:1-11 (2005), which is hereby incorporated by reference in its entirety).

In therapeutic applications, for example, application of a magnetic field to the patient may serve to target drug-carrying magnetic particles to a desired body site. In many cases, the dose of systemically administered chemotherapeutics is limited by the toxicity and negative side effects of the drug. Therapeutically sufficient concentrations of the drugs in the respective tissues often need to be quite high. Magnetic carrier systems should allow targeted drug delivery to achieve such high local concentrations in the targeted tissues, thereby minimizing the general distribution throughout the body. Special magnetic guidance systems can direct, accumulate, and hold the particles in the targeted area, for example, a tumor region (Alexiou et al., J. Nanosci. Nanotechnol. 6:2762 (2006), which is hereby incorporated by reference in its entirety).

EXAMPLES

The following examples are intended to illustrate the invention, and are not intended to limit its scope.

Example 1 Chemicals

Iron pentacarbonyl (Fe(CO)₅), phenyl ether, trimethylamine oxide, decanethiol (DT) tetraoctylammonium bromide (TOA-Br), oleylamine (OAM), oleic acid (OA), trimethylamine oxide dihydreate ((CH₃)₃NO.2H₂O), bovine serum albumin (BSA), 11-mercaptoundecanoic acid (MUA), mercaptobenzoic acid (MBA), dithiobis (succinimidyl propionate) (DSP), and other solvents (hexane, toluene, and ethanol) were obtained form Aldrich and were used as received. Anti-rabbit IgG and rabbit IgG were purchased from Pierce. Protein A and gold nanoparticles were obtained from Ted Pella.

Example 2 Synthesis and Preparation

Fe₂O₃ (γ-Fe₂O₃) nanoparticles and Au nanoparticles were synthesized by known protocols, whereas the preparation of Fe₂O₃@Au nanoparticles was based on a new protocol developed in this work. For the synthesis of Fe₂O₃ nanoparticles, Fe₂O₃ nanoparticles capped with OA (and/or OAM) were prepared based on the modified procedure reported previously (Wang et al., J. Phys. Chem. B 109:21593 (2005), which is hereby incorporated by reference in its entirety). Briefly, 0.74 mL of Fe(CO)₅ and 5.3 mL of OA (and/or OAM) in 40 mL of phenyl ether was stirred at 100° C. under argon purge. The solution was heated to 253° C. and refluxed for 1 h. The solution turned to dark brown. After the solution was cooled to room temperature, 1.26 g of (CH₃)₃NO.2H₂O was added and stirred at 130° C. for 2 h. Temperature was increased to 253° C. and refluxed for 2 h. The reaction solution was stirred overnight. The resulting nanoparticles were precipitated with ethanol and rinsed multiple times. Finally, particles were dispersed in hexane or toluene. For the synthesis of Au nanoparticles, the standard two-phase method reported by Brust and Schriffrin (J. Chem. Soc., Chem. Commun. 1994:801-802, which is hereby incorporated by reference in its entirety) was used. Gold nanoparticles of 2 nm diameter encapsulated with DT monolayer shells (Au_(2nm)-DT) were synthesized.

For the preparation of Fe₂O₃@Au nanoparticles, a modified strategy of thermally-activated processing protocol (Schadt et al., Chem. Mater. 18:5147 (2006); Maye et al., Langmuir 16:490 (2000); Zhong et al., Chem. Commun. 13:1211 (1999), which are hereby incorporated by reference in their entirety) was used. The thermal processing treatment of Au nanoparticles involved molecular desorption, nanoscrystal core coalescence, and molecular re-encapsulation processes in the evolution of nanoparticle precursors at elevated temperatures (149° C.). The thermal processing of small-sized monolayer-protected nanoparticles as precursors (Schadt et al., Chem. Mater. 18:5147 (2006); Maye et al., Langmuir 16:490 (2000); Zhong et al., Chem. Commun. 13:1211 (1999), which are hereby incorporated by reference in their entirety) has recently gained increasing interest for processing nanoparticle size and monodispersity (Clarke et al., Langmuir 17:6048-6050 (2001); Teranishi et al., Adv. Mater. 13:1699-1701 (2001); Fan et al., Chem. Commun. 2006:2323-2325 Terzi et al., J. Phys. Chem. B 109:19397-19402 (2005); Shaffer et al., Langmuir 20:8343-8351 (2004); Chen et al., J. Phys. Chem. B 105:8816-8820 (2001), which are hereby incorporated by reference in their entirety). In a typical thermal processing treatment, 1.4 mL of Au_(2nm)-DT and Fe₂O₃ nanoparticles in toluene with various ratio was placed in a reaction tube. The mixed precursor solution contained Au_(2nm)-DT, OA- and/or OAM-Fe₂O₃ nanoparticles, toluene, and TOA-Br. The tube was then placed in a preheated Yamato DX400 Gravity Convection Oven at 149° C. for 1-hour. Temperature variation from this set point was limited to ±1.5° C. After the 1-hour thermal treatment, the reaction tube was allowed to cool down and the particles were redispersed in toluene. The above approach can also be used to produce Fe₃O₄@Au nanoparticles. The term “Fe-oxide” was used to refer to a variety of iron oxides, including Fe₂O₃ and Fe₃O₄.

Example 3 Preparation of Nanoparticles Capped with Proteins and SERS Labels

The as-synthesized DT-capped iron oxide Au particles were transferred to water by ligand exchange using mercaptoundecanoic acid (MUA) by following a procedure reported by Gittins et al. (Chem. Phys. Chem. 3(1):110-113 (2002), which is hereby incorporated by reference in its entirety), with a slight modification. The nanoparticles were further modified with DSP for protein coupling by ligand exchange. To 1 mL solution of DT-capped iron oxide@Au particles (6 ng/mL) in borate buffer (pH 8.3), 140 μL of 1 mM DSP was added and stirred overnight. The nanoparticles were rinsed with centrifuge and 20 μL of anti-Rabbit IgG (2.4 mg/mL) was pipetted. After overnight incubation, the particles were centrifuged three times and finally resuspended in 2 mM Tris buffer (pH 7.2) with 1% BSA and 0.1% Tween 80. The same method was also used for coating protein A and BSA to Au nanoparticles of 80 nm size. 2.5 μL of 1 mM DSP was added to 1 mL of Au particles (80 nm, 1×10¹⁰/mL) and reacted overnight. 40 μL of 50 mM borate buffer was added and either protein A or BSA was added to make final concentration of protein A or BSA to be ˜25 μg/mL. MBA was used as a Raman label (Ni et al., Anal Chem., 71:4903 (1999), which is hereby incorporated by reference in its entirety). To introduce spectroscopic label onto the Au nanoparticles modified with either protein A or BSA, an ethanolic solution of MBA (10 μg/mL) was added and reacted overnight. Finally, the particles were centrifuged three times and finally re-suspended in 2 mM Tris buffer (pH 7.2) with 1% BSA and 0.1% Tween 80. The resulting protein capped nanoparticles were stored at 4° C.

Example 4 Measurements and Instrumentation

The study of the binding between Au nanoparticles labeled with protein A (or BSA) and MBA (A) and iron oxide Au nanoparticles labeled with anti-rabbit IgG (B) was carried out by mixing (A) and (B). 250 μL of (A) was first diluted in 1750 μL tris buffer before mixing with ˜10 μL of (B). UV-vis spectra were collected immediately following gentle mixing of the solution. Spectroscopic measurements were performed after using magnet to collect the reaction product. For spectroscopic labeling, 0.8 mL of ethanolic solution of MBA was added to 0.5 mL of iron oxide@Au particles (30 mg/mL in toluene), and shaked overnight. The particles were cleaned three times with toluene and ethanol and dispersed in 2 mM borate buffer. The particles were then drop cast on gold on mica surface.

Example 5 Surface-Enhanced Raman Scattering (SERS)

Raman spectra were recorded using the Advantage 200A Raman instrument (DeltaNu). The instrument collects data over 200 to 3400 cm⁻¹. The laser power was 5 mW and the wavelength of the laser was 632.8 nm. In the experiment, the spectrum in the range from 200 to 1500 cm⁻¹ was collected.

Example 6 Transmission Electron Microscopy (TEM)

TEM micrographs of the particles were obtained using a Hitachi H-7000 Electron Microscope operated at 100 kV. The particles dispersed in hexane were drop cast onto a carbon film coated copper grid followed by evaporation at room temperature.

Example 7 Ultraviolet-Visible Spectroscopy (UV-Vis)

UV-Vis spectra were acquired with a HP8453 spectrophotometer. The spectra were collected over the range of 200-1100 nm.

Example 8 Direct Current Plasma-Atomic Emission Spectroscopy (DCP-AES)

The composition of synthesized particles and thin films was analyzed using DCP-AES. Measurements were made on emission peaks at 267.59 nm and 259.94 nm, for Au and Fe, respectively. The nanoparticle samples were dissolved in concentrated aqua regia, and then diluted to concentrations in the range of 1 to 50 ppm for analysis. Calibration curves were constructed from standards with concentrations from 0 to 50 ppm in the same acid matrix as the unknowns. Detection limits, based on three standard deviations of the background intensity are 0.008 ppm and 0.005 ppm for Au and Fe, respectively. Standards and unknowns were analyzed 10 times each for 3 second counts. Instrument reproducibility, for concentrations greater than 100 times the detection limit, results in <2% error.

Example 9 Morphological Characterization of the Core-Shell Magnetic Nanoparticles

Since the thermal processing treatment involved molecular desorption, nanoscrystal core coalescence, and molecular re-encapsulation processes at elevated temperatures, as demonstrated in previous work for gold and alloy nanoparticles (Schadt et al., Chem. Mater. 18:5147 (2006); Maye et al., Langmuir 16:490 (2000); Zhong et al., Chem. Commun. 13:1211 (1999), which are hereby incorporated by reference in their entirety), the examination of the structure and morphology of the evolved nanoparticles is important for the overall assessment of the viability in processing the Fe-oxide@Au nanoparticles. As a control experiment, FIGS. 3A-B show the representative set of TEM images for gold nanoparticles thermally processed from 2-nm sized, DT-capped gold nanoparticles (2.0±0.4 nm). The increased particle size and the high monodispersity of the resulting nanoparticles (6.4±0.4 nm) are consistent with what has been previously reported, demonstrating the effectiveness of the thermal processing condition for processing gold nanoparticles.

As another control experiment, the thermal processing of Fe₂O₃ nanoparticles under the same condition was also examined. FIGS. 4A-B show a representative set of TEM images for Fe₂O₃ nanoparticles by thermally processing of Fe₂O₃ nanoparticles of 4.4 nm size. The observation of insignificant changes in the particle size and the monodispersity of the resulting nanoparticles (4.5±0.5 nm) demonstrate the absence of any size evolution for Fe₂O₃ nanoparticles with the thermal processing conditions used in the present work. The absence of size evolution is likely associated with the lack of significant change in melting temperature for Fe₂O₃ nanoparticles. In other words, Fe₂O₃ nanoparticles are stable under the thermal processing temperature.

The above two control experiments demonstrate that the gold nanoparticles undergo thermally activated coalescence responsible for the growth of Au nanoparticles whereas the Fe₂O₃ nanoparticles remain largely unchanged in this process. In the next experiment, the thermal processing treatment of a controlled mixture of the 2-nm sized gold nanoparticles and the 4-nm sized Fe₂O₃ nanoparticles was examined under the same thermal processing condition. Specifically, a toluene solution of the two precursor nanoparticles (e.g., stock solutions of decanethiolate (DT)-capped Au (2 nm, 158 μM) and OAM and/or OA-capped Fe₂O₃ (5 nm, 6.3 μM), or Fe₃O₄ with a controlled ratio in a reaction tube was heated in an oven at 149° C. for 1 hour. Other constituents in the solution included TOA-Br and DT with controlled concentrations. After cooling to room temperature, the solidified liquid was dispersable in toluene. FIGS. 5A-C show a representative set of TEM micrographs comparing the resulting nanoparticles obtained from the thermal processing treatment with the two precursor nanoparticles. It is evident that highly monodispersed nanoparticles with an average size of 6.2±0.3 nm are obtained from the processing of the mixture using a 25:1 ratio of Au to Fe₂O₃ nanoparticles (FIG. 5C). The precursor Fe-oxide nanoparticles were not observed after the processing treatment of the mixture. This feature is in sharp contrast to the morphological features corresponding to the nanoparticle precursors of DT-capped Au (2.1±0.3 nm) (FIG. 5B) and OA-capped Fe₂O₃ (4.4±0.3 nm) (FIG. 5A).

FIGS. 6A-B show another representative set of TEM images for the nanoparticles thermally evolved from the same precursors but with two different molar ratios of the precursors, Au:Fe₂O₃=25:1 (FIG. 6A) and 132:1 (FIG. 6B). It is evident that the size and monodispersity of the evolved nanoparticles are dependent on the precursor ratios. A higher ratio of Au to Fe₂O₃ nanoparticle precursors clearly favors the formation of larger-sized and more monodispersed nanoparticles.

In addition to manipulating the relative concentrations of Au and Fe₂O₃ to control the thickness of Au shell, the formation of the core-shell nanoparticles with multiple magnetic cores were shown to be possible, depending on the manipulation of a combination of control parameters. Nanoparticles with larger sizes (30-100 nm) have been obtained by controlling the ratio of the precursor nanoparticles and the chemical nature of capping molecules. FIGS. 7A-D show a representative set of TEM images for particles obtained with relatively-lower concentrations of Au (Au:Fe₂O₃=5:1), demonstrating that important roles have been played by both the Au to Fe₂O₃ concentration ratio and the type of capping agent on the final size and monodispersity. It is also noted that the basic feature of these evolved nanoparticles remains unchanged from sample to sample, demonstrating the reproducibility of the method. The average size for the nanoparticles obtained from OA-capped Fe₂O₃ is 31.4±3.0 nm with high monodispersity (FIGS. 7A-B), whereas that from the OAM-capped Fe₂O₃ exhibits sizes of 30 to 100 nm and hexagon-shaped features (FIG. 7C).

By controlling the condition so that the thermal equilibrium can be perturbed (e.g., shorter time, lower temperature, or larger reaction volume), the observed features appear to correspond to the early stage of coalescence of the core-shell nanoparticles. For example, for the thermal evolution in a larger reaction volume, spherical clusters with highly ordered packing morphology were observed (FIG. 7D). The center of the spherical assembly shows indications of interparticle coalescence, in contrast to the loosely-bound nanoparticles spread around the spherical outline. Control experiments showed that under the temperature while Au nanoparticles could be evolved to sizes of up to 10 nm, Fe₂O₃ nanoparticles remained unchanged. Thus, these large-sized particles likely consist of multiple Fe-oxide cores.

Example 10 Characterization of the Surface Chemistry of the Core-Shell Magnetic Nanoparticles

There are two key questions that must be answered about the formation of the core-shell magnetic nanoparticles. The first question concerns whether surface of the nanoparticles are composed of Au shell, and the second question concerns whether the nanoparticle cores include magnetic Fe₂O₃ nanoparticles. To address these questions, both high-resolution TEM (“HRTEM”) and electron diffraction (“ED”) techniques seemed to be ideal for examining the detailed core-shell morphology. While small differences in HRTEM and ED have been observed by comparing the Fe₂O₃@Au nanoparticles with the Au and Fe₂O₃ nanoparticles, the results were not conclusive. XPS technique is also not appropriate because of the depth sensitivity issue. It is also noted that XRD examination of the core-shell nanoparticles was not conclusive either. It is possible that the lattice parameters of the iron oxide core were distorted by the relatively thick Au shell, which is a fundamental issue to be addressed. Detailed experimental data obtained from the examinations of the core-shell nanoparticles is provided in terms of the surface chemistry of the Au shell and the magnetic properties of the core to address the above two questions.

To prove that the resulting nanoparticles include the desired Au shell, two types of measurements were carried out, both of which were based on the surface chemistry of gold-thiolate binding and core-shell composition. First, the core-shell composition was analyzed, for which samples were prepared by assembling the nanoparticles into thin films on a glass substrate using dithiols as linkers/mediators (FIG. 8) (Wang et al., J. Phys. Chem. B 109:21593 (2005); Leibowitz et al., Anal. Chem. 71:5076 (1999); Luo et al., J. Phys. Chem. 108:9669 (2004), which are hereby incorporated by reference in their entirety). The dithiolate-gold binding chemistry involves a sequence of exchanging, crosslinking, and precipitation processes which has previously been demonstrated to occur to Au surface only. Thin film assemblies were observed for those with an Au surface, i.e., Fe₂O₃@Au (FIG. 8, (A)) and Au (FIG. 8, (B)) nanoparticles (or a combination of (A) and (B)). In contrast, there were no thin film assemblies for Fe₂O₃ nanoparticles under the same reaction condition (FIG. 8, (C)).

To analyze the core-shell composition, samples of the dithiol-mediated thin film assemblies of the nanoparticles were dissolved in aqua regia, and the composition was then analyzed using direct current plasma-atomic emission spectroscopy (DCP-AES) technique. The as-processed nanoparticles were also analyzed for comparison. For example, 1,9-nonanedithiol-mediated assembly of nanoparticles into a thin film (Brust et al., J. Chem. Soc. Chem. Commun. 1994:801-802, which is hereby incorporated by reference in its entirety) is selective to Au or Fe₂O₃@Au but not to Fe₂O₃. As shown in Table 1, both Au and Fe were detected, demonstrating that the nanoparticles contain both Fe and Au components. It is therefore evident that the surface of Fe₂O₃ particles must be covered by Au.

TABLE 1 Analysis of Metal Composition in the Fe₂O₃@Au Nanoparticles Atomic d_(shell) (nm) ratio determined by Sample (Au:Fe) TEM DCP-AES As-synthesized 77:23 1.1 1.0 Thin Film 84:16 1.1 1.4

Quantitatively, the Au:Fe ratios for the thin films were slightly higher than those for the as-synthesized particles. The Au shell thickness can be estimated from the Au:Fe ratios based on a spherical core-shell model (Wang et al., J. Phys. Chem. B 109:21593 (2005), which is hereby incorporated by reference in its entirety). The results obtained from the DCP data for both the as-synthesized and the thin film (Table 1) are found to be very close to the values measured from the TEM data.

In the second type of measurements, SERS labels such as MBA were immobilized on the surface of the core-shell nanoparticles via Au-thiolate binding chemistry. FIGS. 9A-B show a representative set of SERS spectra for the core-shell Fe₂O₃@Au nanoparticles labeled with MBA. The SERS for Fe₂O₃@Au nanoparticles (FIG. 9A) showed clearly two peaks at 1084 and 1593 cm⁻¹, which are identical to those observed for the Au nanoparticles (FIG. 9B). These two bands correspond to v(CC) ring-breathing modes of MBA, which are characteristic of the expected signature (Varsanyi, Assignments for Vibrational Spectra of Seven Hundred Benzene Derivatives; John Wiley & Sons: New York, 1974, which is hereby incorporated by reference in its entirety). Controlled experiment with Fe₂O₃ nanoparticles incubated with MBA did not show any of these bands. This observation demonstrates that MBA labels are immobilized on the Au shell of the Fe₂O₃@Au nanoparticles.

Example 11 Protein Binding and Bioseparation Using the Core-Shell Magnetic Nanoparticles

For the targeted bio-separation application, both the protein-binding properties of the gold shell and the magnetic properties of the core in the Fe₂O₃@Au nanoparticles are essential. The recent results of magnetic characterization for similar core-shell Fe-oxide Au nanoparticles (Wang et al., J. Phys. Chem. B 109:21593 (2005), which is hereby incorporated by reference in its entirety) have revealed detailed information for assessing the magnetic properties. In FIGS. 10A-C, a set of photos is shown to illustrate the movement of the nanoparticles dispersed in solutions before and after applying a magnetic field (NdFeB type) to the particles. The core-shell nanoparticles can be fully dispersed in toluene solution (FIG. 10A), which did not respond to external magnetic field of the magnet. However, the suspension of the same nanoparticles in ethanol-toluene (FIG. 10B), which has an increased magnetic susceptibility due to aggregation, showed that the suspended particles moved towards the wall near the magnet gradually (FIG. 10C), eventually leaving a clear solution behind.

This test result demonstrated clearly that the Fe₂O₃@Au nanoparticles are magnetically active, which is desired for the targeted bio-separation application. Similar results were also obtained for the core-shell nanoparticles prepared using different precursor ratios.

To further demonstrate the viability of the Fe₂O₃@Au nanoparticles for magnetic bio-separation, the following proof-of-concept demonstration experiment exploits both the magnetic core and the bio-affinity of the gold shell. In this experiment, the gold-based surface protein-binding reactivity and the Fe-oxide based magnetic separation capability were examined. The DT-capped Fe₂O₃@Au particles were first converted to water-soluble particles by ligand exchange reaction with MUA. The ligand exchange reaction involved replacement of the original capping molecules (OAM and OA) on Fe₂O₃@Au nanoparticles by acid functionalized thiols. To prove the ligand exchange on the nanoparticle surface, FIGS. 11A-B show a representative set of FTIR spectra of the OAM/OA-capped Fe₂O₃ @Au nanoparticles before and after the ligand exchange reaction. After the exchange reaction, the band at 3004 cm⁻¹ corresponding to the C—H stretching mode next to the double bond from OA and OM capping molecules (FIG. 11A) are clearly eliminated (FIG. 11B). In the meantime, the band at 1709 cm⁻¹ corresponding to the carboxylic acid group of MUA is detectable after the exchange reaction. Furthermore, the spectral change in the 1300-1560 cm⁻¹ region seemed to support the presence of bands corresponding to the symmetric and asymmetric stretching modes in the carboxylate groups of MUA.

These observations demonstrate the successful exchange of the MUA with the original ligands on the nanoparticles. This is further evidenced by the fact that the post-exchanged core-shell nanoparticles became water-soluble.

The MUA-capped Fe₂O₃@Au nanoparticles in water underwent further exchange reaction with a protein-coupling agent, DSP, forming a DSP-derived monolayer on the gold surface. Antibody (anti-rabbit IgG) was then immobilized onto the resulting nanoparticles via coupling with the surface DSP, forming Ab-immobilized core-shell nanoparticles.

The Ab-immobilized core-shell nanoparticles were reacted with Au particles capped with both protein-A and a Raman label, e.g., MBA. FIG. 12 illustrates the reactions and product separation of the antibody-labeled Fe₂O₃@Au nanoparticles in two different reaction systems: reaction with protein A capped gold nanoparticles (A1-B1), and reaction with BSA capped gold nanoparticles (A2-B2). In each case, magnetic field was applied to collect the magnetically-active products for SERS analysis.

FIG. 13 shows a representative set of UV-Vis spectra monitoring the reaction progress. Results from control experiments are also included for comparison, in which the Au particles capped with BSA (bovine serum albumin) and MBA were used to replace the Au particles capped with protein A while maintaining the rest of the conditions. The specific reactivity between Fe₂O₃@Au nanoparticles capped with anti-rabbit IgG (Ab) and Au nanoparticles capped with protein-A is clearly evidenced by the gradual decrease of the surface plasmon (SP) resonance band at 535 nm and its expansion at the longer wavelength region (A1). This finding is in sharp contrast to the lack of any change in SP band for the reaction between Fe₂O₃@Au nanoparticles capped with anti-rabbit IgG and Au nanoparticles capped with BSA (A2). In contrast to the specific binding of anti-rabbit IgG to protein-A, there is no specific binding between BSA and anti-rabbit IgG.

FIG. 14 shows a representative set of SERS spectra of the products collected by applying the magnet to the reaction solution for the Fe₂O₃@Au nanoparticles capped with anti-rabbit IgG and Au nanoparticles capped with protein-A. The spectrum from the control experiment is also included for comparison, in which the Au nanoparticles capped with BSA protein and MBA label were used to react with Fe₂O₃@Au nanoparticles capped with anti-rabbit IgG while maintaining the reaction conditions.

The product of the reaction collected by a magnet showed the expected SERS signature of MBA (B1), corresponding to v(C—C) ring-breathing modes of MBA. This finding is in sharp contrast to the absence of SERS signature in the control experiment (B2). These two findings clearly demonstrate the viability of exploiting the magnetic core and gold shell of the Fe₂O₃@Au nanoparticles for interfacial bio-assay and magnetic bio-separation.

In conclusion, a novel strategy based on the thermally-activated hetero-coalescence between Au and Fe₂O₃ nanoparticles has been demonstrated for the fabrication of monodispersed magnetic core-shell nanoparticles, Fe₂O₃@Au. Similar results have also been observed for Fe₃O₄ nanoparticle cores. In comparison with the previous sequential synthesis method involving reduction and deposition of gold onto pre-synthesized iron oxide nanoparticles (Wang et al., J. Phys. Chem. B 109:21593 (2005), which is hereby incorporated by reference in its entirety), the nanoparticles made by the thermal approach can have similar core-shell structure with gold shell and iron-oxide core, and show similar behavior in forming thin films due to the gold shell. Some of the major differences between the two nanoparticle products include the core-shell size range and the surface capping structure. Due to the unique processing environment, nanoparticles with much larger sizes can be made. The capping structure can be tailored differently in the two cases. These core@shell nanoparticles consist of magnetically-active Fe-oxide core and thiolate-active Au shell, which were shown to exhibit the Au surface binding properties for interfacial biological reactivity and the Fe-oxide core magnetism for magnetic bio-separation. These magnetic core-shell nanoparticles have therefore shown the viability for utilizing both the magnetic core and gold shell properties for interfacial bio-assay and magnetic bio-separation. These findings are entirely new, and could form the basis of fabricating size, magnetism, and surface tunable magnetic nanoparticles for bio-separation and biosensing applications.

Although the invention has been described in detail for the purpose of illustration, it is understood that such detail is solely for that purpose, and variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention which is defined by the following claims. 

1. Core-shell nanoparticles, each core-shell nanoparticle comprising: a gold shell; a plurality of discrete, nonconcentric, iron oxide-containing cores, each core being within and surrounded by said gold shell; and a ligand cap over said gold shell.
 2. The core-shell nanoparticles according to claim 1, wherein the nanoparticles are present in a monodispersion with controlled diameters ranging from 5 nm to 100 nm.
 3. The core-shell nanoparticles according to claim 1, wherein the iron oxide-containing cores are magnetic, paramagnetic, or superparamagnetic.
 4. The core-shell nanoparticles according to claim 1, wherein the iron oxide-containing core comprises a compound selected from the group consisting of Fe₃O₄ and Fe₂O₃.
 5. The core-shell nanoparticles according to claim 4, wherein the iron oxide-containing core comprises Fe₂O₃.
 6. The core-shell nanoparticles according to claim 1, wherein the ligand cap is selected from the group consisting of decanethiolate, oleylamine, oleic acid, acrylates, N,N-trimethyl(undecylmercapto)ammonium (TUA), tetrabutylammonium tetrafluoroborate (TBA), tetramethylammonium bromide (TMA), cetyltrimethylammonium bromide (CTAB), citrates, poly methacrylate, ascorbic acid, DNA, 2-mercaptopropionic acid (MPA), 3-mercaptopropionic acid (MPA), 11-mercaptoundecanoic acid (MUA), 10-mercaptodecane-1-sulfonic acid, 16-mercaptohexadecanoic acid, diimide, N-(2-mercaptopropionyl)glycine (tiopronin), 2-mercaptoethanol, 4-mercapto-1-butanol, dodecyl sulfate, amino acids, homocysteine, homocystine, cysteine, cystine, glutathione, mercaptobenzoic acid (MBA), Protein A, bovine serum albumin (BSA), and anti-rabbit-IgG (Ab).
 7. The core-shell nanoparticles according to claim 6, wherein the ligand cap is selected from the group consisting of decanethiolate, oleylamine, and oleic acid.
 8. The core-shell nanoparticles according to claim 7, wherein the ligand cap is decanethiolate.
 9. The core-shell nanoparticles according to claim 7, wherein the ligand cap is oleylamine.
 10. The core-shell nanoparticles according to claim 7, wherein the ligand cap is oleic acid.
 11. The core-shell nanoparticles according to claim 1 further comprising: a first binding material bound to the ligand-capped shell.
 12. The core-shell nanoparticles according to claim 11, wherein the first binding material is selected from the group consisting of proteins, peptides, antibodies, and antigens. 